Magnetoimpedance effects in a CoNiFe nanowire array

This report describes the growth of CoNiFe nanowires into highly ordered porous anodic alumina oxide (AAO) templates by DC electrodeposition at a pH value of 2.6. Scanning electron microscopy (SEM) observations revealed that the wires have diameters of approximately 270–290 nm and a length of 25 μm. The energy dispersive X-ray (EDX) analysis indicated that the composition of the nanowires is Co12Ni64Fe24. Electrical contacts were created on both sides of the nanowire array, and their magnetoimpedance (MI) properties were investigated. The impedance value was initially 1.2 ohm at low frequency and increased to approximately 1000 ohm for a 33-MHz driving current frequency under no applied magnetic field. All the MI curves exhibited single peak behaviour due to the high shape anisotropy. The maximum MI change at the 33-MHz driving current frequency was 2.72%. The maximum resistance change was 5.4% at 33 MHz.

► CoNiFe nanowires were produced by electrodeposition method.
► Magnetoimpedance effect of nanowires arrays were investigated.
► Single peak behaviour was observed in the magnetoimpedance curve.
► Nanowire arrays exhibit uniaxial magnetic anisotropy along the wire axis.