![عکس صفحه اول مقاله: Synthesis of VBO3–carbon composite by ball-milling and microwave heating and its electrochemical properties as negative electrode material of lithium ion batteries Synthesis of VBO3–carbon composite by ball-milling and microwave heating and its electrochemical properties as negative electrode material of lithium ion batteries](/preview/png/1615336.png)
Ball-milling and subsequent microwave heating processes have been applied to synthesize VBO3–C composite. The samples were characterized by X-ray diffraction, scanning electron microscope, transmission electron microscope, inductively coupled plasma mass spectroscopy, and electrochemical methods. The VBO3–C composite was successfully prepared after 30 min ball-milling and 13 min microwave heating. The synthesized VBO3–C composite was composed of well crystallized VBO3 particles with well dispersed amorphous carbon and exhibited higher reversible capacity (625 mAh g−1) and improved cyclic performance than those in previous study.
Synthesis of VBO3-carbon composite by ball-milling and microwave heating and its electrochemical properties as negative electrode material of lithium ion batteries.Figure optionsDownload as PowerPoint slideHighlights
► VBO3–C composite was synthesized by ball-milling and subsequent microwave heating.
► The synthesis was accelerated with increasing B/V molar ratio in the precursor.
► VBO3–C composite was composed of crystallized VBO3 particles with amorphous carbon.
Journal: Journal of Alloys and Compounds - Volume 542, 25 November 2012, Pages 132–135