Cost effective, ruthenium metal free rhodamine B dye has been chemically adsorbed on ZnO films consisting of nanobeads to serve as a photo anode in dye sensitized solar cells. These ZnO films were chemically synthesized at room temperature (27 °C) on to fluorine doped tin oxide (FTO) coated glass substrates followed by annealing at 200 °C. These films consisting of inter connected nanobeads (20–40 nm) which are due to the agglomeration of very small size particles (3–5 nm) leading to high surface area. The film shows wurtzite structure having high crystallinity with optical direct band gap of 3.3 eV. Optical absorbance measurements for rhodamine B dye covered ZnO film revealed the good coverage in the visible region (460–590 nm) of the solar spectrum. With poly-iodide liquid as an electrolyte, device exhibits photon to electric energy conversion efficiency (η) of 1.26% under AM 1.5G illumination at 100 mW/cm2.
► Synthesis of ZnO film was done at room temperature (27 °C).
► Simple and inexpensive chemical bath deposition method was employed.
► The as deposited film consists of mixed phases of hydroxide and oxide.
► The post annealing was done at 200 °C in order to remove hydroxide phase.
► Low-cost, metal free Rhodamine B dye was used for DSSC application.
Journal: Journal of Alloys and Compounds - Volume 510, Issue 1, 5 January 2012, Pages 33–37