The Mg-added (0%, 5%, and 10%) MgB2/Cu superconducting wires were prepared by the powder-in-tube (PIT) method. Vickers micro-indentation tests were performed on the samples with different peak loads at room temperature. The loading–unloading (P–h) curves were analyzed by the displacement approach to indentation. It was found that hardness (H) and the effective elastic modulus (E) values increased with Mg-added. In addition, these values showed peak load dependence (i.e. indentation size effect (ISE)).
Figure optionsDownload as PowerPoint slideResearch highlight▶ Mechanical properties of Mg-addition MgB2 superconducting wires were investigated by Vickers hardness test. It was found that hardness (H) and the effective elastic modulus (E) values increased with Mg-added. These values showed peak load dependence (i.e. indentation size effect (ISE).
Journal: Journal of Alloys and Compounds - Volume 509, Issue 5, 3 February 2011, Pages 1691–1695