![عکس صفحه اول مقاله: Synthesis and microwave absorbing properties of FeCo alloy particles/graphite nanoflake composites Synthesis and microwave absorbing properties of FeCo alloy particles/graphite nanoflake composites](/preview/png/1619200.png)
Exfoliated graphite was processed into nano-sized flakes by jet milling, ultrasonication and acid treatments, and then FeCo alloy particles were uniformly deposited onto the surface of the prepared graphite nanoflakes (GNFs) by a co-deposition and subsequent annealing process in reducing atmosphere. The FeCo-GNFs composites demonstrate good soft magnetic performance and effective microwave absorption, especially in the lower frequency range. The strongest absorption reaches −30.6 dB at 7.4 GHz with a coating thickness of 2 mm. Furthermore, effective microwave absorption at different frequency bands can be acquired by adjusting the coating thicknesses and filling ratios of FeCo-GNFs absorber. Considering the low cost and high efficiency, the FeCo-GNFs composites have great potential as microwave absorber for practical applications.
Research highlights▶ Worm-like exfoliated graphite is separated into graphite nano flakes (GNFs). ▶ FeCo-GNFs composites are synthesized by a simple method. ▶ FeCo-GNFs have a good microwave absorption, especially in lower frequency range.
Journal: Journal of Alloys and Compounds - Volume 509, Issue 2, 12 January 2011, Pages 494–498