![عکس صفحه اول مقاله: Silver nanoparticles prepared by chemical reduction-protection method, and their application in electrically conductive silver nanopaste Silver nanoparticles prepared by chemical reduction-protection method, and their application in electrically conductive silver nanopaste](/preview/png/1620674.png)
Ag nanoparticles were prepared in a water-phase system with a mixture of silver–ammonia complex, sodium borohydride, and lauric acid according to molar feed ratio of approximately 6:3:1. The mechanism of preparation and separation by chemical reduction-protection method was explored. The as-synthesized Ag nanoparticles were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) and UV–vis spectroscopy, respectively. It was found that the size of high purity Ag particles was ranging from 30 to 50 nm with slight agglomeration. In addition, the as-synthesized wet Ag nanoparticles were dispersed stably in organic vehicle to formulate electrically conductive nanopaste. Upon direct-written and sintered, the array pattern of the nanopaste with the resolution of about 30 μm was achieved with the electrical resistivity in the order of magnitude of 10−5 Ω cm.
Journal: Journal of Alloys and Compounds - Volume 494, Issues 1–2, 2 April 2010, Pages 84–87