The influence of prior cold working on the friction and wear behavior of Cu–0.65 wt.%Cr alloy under dry sliding against a steel disk was investigated on a pin-on-disk wear tester. The worn surfaces and debrises of Cu–Cr alloy were analyzed by scanning electron microscope (SEM) and energy dispersive X-ray (EDX) spectrum. The results indicated that prior cold working and aging had an effect on the hardness and wear resistance of Cu–Cr alloy; in other words hardness and wear rate increased with the amount of cold working. At constant aging temperature, the wear rate of Cu–Cr alloys increase with cold working and reached maximum at 50% cold working. At constant amount of cold working aged specimens at 500 °C shows higher wear resistance than 450 °C. Crack initiation and propagation in the tribolayer and at the interface of subsurface and tribolayer was the dominant mechanism during the sliding process.
Journal: Journal of Alloys and Compounds - Volume 480, Issue 2, 8 July 2009, Pages 505–509