Ba(Ce0.8−xSnx)Y0.2O3−σ (x = 0, 0.05, 0.10, 0.15, 0.20, 0.25) powders were prepared by solid state reaction method. The powder samples with Sn element still keep pervoskite-type configuration after boiling in water for 3 h while the BaCe0.8Y0.2O3−σ powders apparently decompose into amorphous phases, which indicates the oxides doped with Sn exhibit good chemical stability. Thermal gravity analysis indicates the compounds with Sn possess better chemical stability in CO2 compared with BaCe0.8Y0.2O3−σ. The BaCe0.7Sn0.1Y0.2O3−σ sample displays a conductivity of 0.007 S/cm at 700 °C in wet hydrogen. Although the relative density of BaCe0.8Y0.2O3−σ only reaches 88.3% after sintering at 1400 °C, the Ba(Ce0.8−xSnx)Y0.2O3−σ samples exhibit relative densities as high as 96.0%. A fuel cell with BaCe0.7Sn0.1Y0.2O3−σ electrolyte was prepared by a suspension spray combining with in situ sintering method and tested in humid hydrogen. Its output and interface resistance are 470 mW/cm2 and 0.13 Ω cm2 at 700 °C, respectively. The short-term performance test also indicates it has good stability as well as desirable compatibility between electrolyte and electrodes.
Journal: Journal of Alloys and Compounds - Volume 473, Issues 1–2, 3 April 2009, Pages 323–329