The differential speed rolling (DSR) with a roll speed ratio of 1.167 was carried out on an AZ31B magnesium alloy in order to investigate its effects on the formability. Compared with the normal rolled sheet exhibiting approximately the same average grain size, the Erichsen values of the DSR processed sheet with an inclination of basal pole in the rolling direction significantly increased by about 1.5 and 1.9 times at room temperature and at 423 K, respectively. The deep-drawing temperature limit for a drawing ratio of 1.5 was also lowered from 443 K to 423 K. The improvement of the press formability at low temperatures can be attributed to the texture modifications, which led to a lower 0.2% proof stress, a larger uniform elongation, a smaller Lankford value and a larger strain hardening exponent.
Journal: Journal of Alloys and Compounds - Volume 470, Issues 1–2, 20 February 2009, Pages 263–268