Structures, electrical and thermal expansion properties of Sr-doped La2Mo2O9 oxide-ion conductors

The oxide-ion conductors (La1−xSrx)2Mo2O9−δ (x = 0.01-0.08) were prepared by means of a conventional solid-state reaction. The effects of Sr doping for La site on the structures, electrical and thermal expansion properties of the oxide-ion conductor La2Mo2O9 were investigated using X-ray diffraction, direct current four-probe method, thermal dilatometer and scanning electron microscopy, respectively. The results show that the lattice constants were first decreased, then increased, and decreased again with the increase of Sr doping content. The solid solubility of Sr in (La1−xSrx)2Mo2O9−δ is x = 0.07. The sinterability of samples is markedly improved with the increase of Sr doping content. The sintered density of sample x > 0.07 is higher than 96% of its theoretical density. When x > 0.02, doping Sr in La2Mo2O9 can inhibit the excessive growth of grains, thus increases the sintered density of samples. The structural transition temperature shifts to the low side with the increase of Sr doping content, and the phase transition is completely suppressed when the doping content reaches 0.07. The conductivity of sample increases with the increase of Sr doping content. The conductivity of sample x = 0.07 reaches a maximum of 0.078 S/cm and 0.101 S/cm at 800 °C and 850 °C, respectively. In this study, it was demonstrated that doping 7 mol% Sr for La site not only can completely suppress the structural phase transition in La2Mo2O9, but also can effectively enhance electrical conductivity of samples at higher temperature.