Effect of initial as-cast microstructure on semisolid microstructure of AZ91D alloy during the strain-induced melt activation process

The effects of different as-cast microstructures which were initially cast in graphite, metal, sand and firebrick moulds, respectively on the semisolid microstructure of AZ91D alloy, have been investigated during the strain-induced melt activation (SIMA) process. The experimental results showed that the moulds with high cooling capacity could produce the fine-grained as-cast microstructure in which the fine α-Mg dendrites were surrounded by a narrow layer of eutectic mixtures. After compressive deformation, in the fine-grained as-cast microstructure, the more systemic strain energy would be gradually accumulated and abundantly stored due to uniform inner crystal lattice distortion, so the recrystallization was easily induced by the stored strain energy at the elevated temperature. As a channel for the diffusion of atoms, the subgrain boundary along which Al element was enriched, foremost melted above the eutectic temperature and resulted in the separation of neighboring subgrains from primary dendrites. Therefore, the refining role of recrystallization on the microstructural evolution from dendrite to globular particles in morphology was easier to play in the fine-grained as-cast microstructure, which was advantageous for the production of fine-grained semisolid microstructure. Additionally, in the fine-grained as-cast microstructure, the melting fracture of narrow secondary dendritic arms was easy to occur in their roots, which also attributed to the production of fine globular grains in semisolid microstructure from primary dendrites. The finer dendrites in the initial as-cast alloy could evolve into the finer globular grains with relatively small grain size distribution range in the semisolid microstructure during partial remelting; therefore, the finer the dendrites in the initial as-cast microstructure, the better were the tensile properties of the evolved semisolid microstructure.