Microstructure and mechanical properties of ultrafine grained Mg97Y2Zn1 alloy processed by equal channel angular pressing
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The Mg97Y2Zn1 alloy processed by equal channel angular pressing (ECAP) has been investigated. It was found that the blocks of secondary phase were broken into uniform distributed sections after ECAP. The Mg97Y2Zn1 alloy processed by ECAP obtained ultrafine grains and exhibits excellent mechanical properties. The average grain size of about 330Â nm, yield strength (YS) of 400.3Â MPa and ultimate tensile strength (UTS) of 450.0Â MPa were obtained by two-step ECAP of 4 passes at 623Â K and 2 passes at 603Â K. The long-period stacking (LPS) structures contribute to the formation of ultrafine grains in ECAP processed Mg97Y2Zn1 alloy. The results demonstrate that ECAP instead of rapid solidified powder metallurgy (RS/PM) can refine grain size and enhance the strength of Mg97Y2Zn1 alloy. It was also found that the elongation of alloy is decreased with increasing pass number. It was found that cracks were preferentially initiated and propagated in the interior of X-phase during the process of ECAP.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 440, Issues 1â2, 16 August 2007, Pages 94-100
Journal: Journal of Alloys and Compounds - Volume 440, Issues 1â2, 16 August 2007, Pages 94-100
نویسندگان
Bin Chen, Dongliang Lin, Xiaoqin Zeng, Chen Lu,