Intermediate temperature tribological behavior of carbon nanotube reinforced plasma sprayed aluminum oxide coating
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Tribological behavior of plasma sprayed carbon nanotube (CNT) reinforced aluminum oxide (Al2O3) composite coatings was examined at room temperature, 573 K and 873 K using tungsten carbide (WC) ball-on-disk tribometer. The weight loss due to wear of Al2O3 coating was found to be increasing with the temperature while Al2O3-CNT coating showed a decreasing trend in the weight loss with the temperature. Relative improvement in the wear resistance of Al2O3-CNT coating compared to Al2O3 coating was found to be 12% at room temperature which gradually increased to â¼Â 56% at 573 K and â¼Â 82% at 873 K. Protective layer as a result of tribo-chemical reaction was observed on the wear track of both of the coatings. The improvement in the wear resistance of Al2O3-CNT coating was attributed to three phenomena viz. (i) higher hardness at the elevated temperature as compared to Al2O3 coating, (ii) larger area coverage by protective film on the wear surface at the elevated temperature and (iii) CNT bridging between splats. The coefficient of friction (COF) of Al2O3 coating was nearly constant at room and elevated temperature whereas COF for Al2O3-CNT coating decreased at the elevated temperature (873 K).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 204, Issue 11, 25 February 2010, Pages 1847-1855
Journal: Surface and Coatings Technology - Volume 204, Issue 11, 25 February 2010, Pages 1847-1855
نویسندگان
Anup Kumar Keshri, Virendra Singh, Jun Huang, Sudipta Seal, Wonbong Choi, Arvind Agarwal,