Mechanical and tribological properties of multilayered TiSiN/CrN coatings synthesized by a cathodic arc deposition process

The monolayered TiSiN and multilayered TiSiN/CrN were synthesized by cathodic arc evaporation. The Ti/Si (80/20 at.%) and chromium targets were used as the cathodic materials. With the different I[TiSi]/I[Cr] cathode current ratios of 1.8, 1.0, and 0.55, the multilayered TiSiN/CrN coatings possessed different multilayer periods (Λ) of 8.3 nm, 6.2 nm, and 4.2 nm. From XRD and TEM analyses, both the monolayered TiSiN and multilayered TiSiN/CrN revealed a typical columnar structure and B1-NaCl crystalline, no peaks of crystalline Si3N4 were detected. Among the multilayered TiSiN/CrN coatings, the multilayered coating with Λ = 8.3 nm possessed higher hardness of 37 ± 2 GPa, higher elastic modulus of 396 ± 20 GPa and the lower residual stress of − 1.60 GPa than the monolayered (Ti0.39Si0.07)N0.54 coating(− 7.25 GPa). Due to the higher Cr/(Ti +Cr + Si) atomic ratio, the multilayered TiSiN/CrN with Λ = 5.5 nm possessed the lowest friction coefficient. But the lowest of wear rate was obtained by the multilayered TiSiN/CrN with Λ = 8.3 nm, because of higher H3/E⁎2 ratio of 0.323 GPa. The monolayered TiSiN possessed the highest wear rate of 2.87 μm2/min. Therefore, the mechanical and tribological property can be improved by the design of multilayered coating.