Effects of the ingot phase transition on microstructure and magnetic properties of CeNdFeB melt-spun ribbons
موضوعات مرتبط
مهندسی و علوم پایه فیزیک و نجوم فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
Effects of the ingot phase transition on microstructure and magnetic properties of CeNdFeB melt-spun ribbons
چکیده انگلیسی
The paper studies the phase transition of ingot with the composition (Ce50Nd50)30FebalCo4Ga0.2B0.92 after the annealing treatment at 1050 °C. The melt-spun ribbons which is prepared by the two treatment status ingots. The phase structure and microstructure morphologies of the ingots and melt-spun ribbons were analysed and observed by XRD and SEM. It was found that the grain size of the ribbons is on the nanometer scale. The EDS results show that there are four different phases in the ingot: (CeNd)2Fe14B, α-Fe, Ce-rich phase and Nd-rich phase. After the annealing treatment, α-Fe, Ce-rich phase, and Nd-rich phase were obviously reduced and the contents of the main phase was significantly increased in the annealed ingot compared with the unanneal treatment ingot. The VSM results show that there is a peak waist in the ribbon which is prepared by the untreated ingot. Because the ingot is uneven, the ribbons may have the secondary phase, the Hcj is 8394 Oe. But the demagnetization curves of the ribbons, which is prepared by the annealed ingot, is relatively smooth and without the soft magnetic phase and the Hcj is 12,528 Oe, which is higher than the unanneal treatment ingot. We can know that the ingot with fine organization is the key factors to preparing high-performance ribbons.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Physica B: Condensed Matter - Volume 476, 1 November 2015, Pages 150-153
نویسندگان
, , , , , , ,