Nanotwinning in CdS quantum dots

High resolution transmission electron microscopy, X-ray diffraction and photoluminescence measurements are carried out in order to study the defects in CdS quantum dots (QDs), synthesized in cubic phase by chemical co-precipitation method. The nanotwinning structures in CdS quantum dots (∼2.7 nm) are reported for the first time. Mostly CdS QDs are characterized by existence of nanotwin structures. The twinning structures are present together with stacking faults in some QDs while others exist with grain boundaries. Raman spectroscopy analysis shows intense and broad peaks corresponding to fundamental optical phonon mode (LO) and the first over tone mode (2LO) of CdS at 302 cm−1 and 605 cm−1 respectively. A noticeable shift is observed in Raman lines indicating the effect of phonon confinement. Fourier transform infrared spectroscopy analysis confirms the presence of Cd–S stretching bands at 661 cm−1 and 706 cm−1. The photoluminescence spectrum shows emission in yellow and red regions of visible spectrum. The presence of stacking faults and other defects are explained on the basis of X-rays diffraction patterns and are correlated with photoluminescence spectrum. These nanotwinning and microstructural defects are responsible for different emissions from CdS QDs.