Magnetic and electrical behavior of La1−xAxMnO3 (A=Li, Na, K and Rb) manganites

With a view to understand the magnetic and electrical behavior of monovalent substituted lanthanum manganites, a series of materials were prepared by sol–gel route by sintering at 1200 °C. The X-ray diffraction data were analyzed using Rietveld refinement technique and it has been found that all the samples were found to crystallize into rhombohedral structure with R3¯c space group. The values of ferro to paramagnetic (TC) and metal–insulator transition (TP) temperatures were obtained using ac susceptibility and electrical resistivity data, respectively. It has been found that sodium-, potassium- and rubidium-doped samples exhibit two peaks in the electrical resistivity vs. temperature plots. The observed behavior has been explained on the basis of oxygen deficiency present in the samples. The electrical resistivity data were analyzed using various theoretical models and it has been concluded that the electrical resistivity data in the low-temperature regime (TTP) were explained using variable range and small polaron hopping mechanisms.