Numerous experimental results have suggested that the Jc of YBa2Cu3O7 (YBCO) films is significantly higher near the film–substrate interface than in the remainder of the film. We previously proposed that this effect is due to interfacial pinning enhancement caused by stress and the resulting misfit dislocations at the heteroepitaxial interface. To test this hypothesis we have used a non-superconducting PrBa2Cu3O7−δ (PrBCO) buffer layer to minimize the lattice mismatch with YBCO. We find that the PrBCO layers lower Jc of the 0.4 μm YBCO films in a predictable way, and that, if sufficiently thick (∼0.5 μm), they eliminate interfacial enhancement altogether. Our interpretation of this result is that the defects responsible for interfacial enhancement of flux pinning originate at the bottom of the non-superconducting PrBCO layer, which screens the pinning centers from vortices in YBCO. This result demonstrates that the pinning enhancement arises from stress at the film–substrate interface.
Journal: Physica C: Superconductivity - Volume 469, Issues 23–24, 1 December 2009, Pages 2033–2036