عنوان انگلیسی مقاله ISI
Formation of defects in precursors for melt-textured RE-Ba-Cu-O superconductors and effect of organic binder addition
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
فیزیک و نجوم
فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
On the processing melt-textured RE-Ba-Cu-O bulk superconductors, we investigated the formation of defects in green bodies during powder compression process and the effect of the defects on the final bulk products. Two kinds of Y-Ba-Cu-O powders with fine and large particle sizes and the granules of binder-added fine powder were uniaxially pressed into tablets (20Â mm in diameter) under different pressures from 31 to 125Â MPa. When the fine powder was pressed at pressures above 62Â MPa, several defects such as lamination, capping and vertical cracking were found in green bodies. The defects in green bodies partially remained after melt-processing and lowered the field-trapping abilities of melt-textured bulk samples. The addition of organic binder is very effective method to reduce the defects in green bodies.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Physica C: Superconductivity and its Applications - Volumes 463â465, 1 October 2007, Pages 308-313
Journal: Physica C: Superconductivity and its Applications - Volumes 463â465, 1 October 2007, Pages 308-313
نویسندگان
S. Nariki, N. Sakai, M. Murakami, I. Hirabayashi,