Ti-sheathed monocore MgB2 wires with improved magnetic critical current density (Jc) have been fabricated by in situ powder-in-tube (PIT) method and characterized by magnetization, X-ray diffraction, scanning electron microscopy and electrical resistivity measurements. For the best wire, the magnetic Jc values at 5 K and fields of 2 T, 5 T, and 8 T are 4.1 × 105 A/cm2, 7.8 × 104 A/cm2, and 1.4 × 104 A/cm2, respectively. At 20 K and fields of 0.5 T and 3 T, the Jc values are about 3.6 × 105 A/cm2 and 3.1 × 104 A/cm2, respectively, which are much higher than those of the Fe-sheathed mono-core MgB2 wires fabricated with the same in situ PIT process and under the same fabricating conditions. It appears that the overall Jc for the average Ti-sheathed wires is comparable to that of the Fe-sheathed wires. Our X-ray diffraction and scanning electron microscopy analysis indicates that Jc in the Ti-sheathed MgB2 wires can be strongly suppressed by MgO impurities and micro-cracks.
Journal: Physica C: Superconductivity - Volume 457, Issues 1–2, 15 June 2007, Pages 47–54