Effect of radiation induced crosslinking and degradation of ETFE films

In this study the ETFE film with 125 μm of thickness was placed inside a nylon bag and filled with either acetylene, nitrogen or oxygen. Following the procedure, the samples were irradiated at 5, 10 and 20 kGy. The physical and chemical properties of the modified and pristine films were evaluated by rheological and thermal analyses (TG and DSC), X-ray diffraction (XRD) and infrared spectroscopy (IR-ATR). In rheological analysis the storage modulus (G′) indicates opposite profiles when the atmospheres (acetylene and oxygen) are evaluated according to the absorbed dose. For the samples submitted to radiation under oxygen atmosphere it is possible to observe the degradation process with the low levels of the storage modulus. The changes in the degree of crystallinity were verified in all modified samples when compared to the pristine polymer and this behavior was confirmed by DSC analysis. A decrease in the intensity of crystalline peak by X-ray diffraction was observed.