Tailoring the properties of gelatin films for drug delivery applications: Influence of the chemical cross-linking method

Two types of chemically cross-linked gelatin films were prepared and characterized. The first type of films was cross-linked with 1-ethyl-3-(3-dimethyl aminopropyl)carbodiimide hydrochloride (EDC) under heterogeneous conditions and are named Gel-E. In the second type of films, gelatin was previously functionalized with methacrylamide side groups by the reaction with methacrylic anhydride and for that is named Gel-MA. The modified gelatin was subsequently cross-linked by a photoinitiated radical polymerization.These films were characterized relatively to their degree of cross-linking, buffer uptake capacity, resistance to hydrolytic and proteolytic degradation, and mechanical and thermal properties. Results show that the employed cross-linking method, together with the degree cross-linking, dictate the final properties of the films. Gel-E films have significant lower buffer uptake capacities and higher resistance to collagenase digestion when compared to Gel-MA films. Additionally, Gel-E films exhibit higher values of stress at break and lower strains at break. Moreover, the films properties could be modified by varying the extent of the chemical cross-linking, which in turn could be controlled by varying the concentration of EDC, for the first type of films (Gel-E), or by using gelatins with different degrees of functionalization, in the case of the second type of films (Gel-MA).

Figure optionsDownload as PowerPoint slide