In recent years, thiomers have received considerable interest due to advantageous characteristics, such as improved mucoadhesive and permeation enhancing properties. Thiolated polymers, however, are characterized by an ionic charge which represents for various applications a great limitation. The aim of this study was therefore to synthesize a novel thiolated polymer not exhibiting ionizable groups. Hydroxyethylcellulose (HEC) was chosen as polymer backbone. The chemical modification was achieved by the replacement of hydroxyl groups on the carbohydrate structure with thiol moieties, using thiourea as thiolating reagent. The resulting thiolated hydroxyethylcellulose (HEC-SH) was characterized in vitro regarding its gelling properties, swelling behaviour, mucoadhesion on freshly excised porcine intestinal mucosa and permeation enhancing effect across rat intestinal mucosa. The new thiomer displayed up to 131.58 ± 11.17 μmol thiol groups per gram polymer, which are responsible for the observed in situ gelling capacity. The swelling behaviour and the mucoadhesive properties of tablets based on HEC-SH were 1.5-fold and 4-fold improved compared with unmodified HEC, respectively. The permeation enhancing effect of 0.5% (m/v) HEC-SH on rhodamine 123 (Rho-123) transport was 1.9-fold improved compared with buffer only. According to these results, HEC-SH seems to represent a promising tool for the development of in situ gelling, mucoadhesive delivery systems with permeation enhancing properties.
Synthetic pathway of thiolated hydroxyethylcellulose (HEC-SH).Figure optionsDownload as PowerPoint slide
Journal: European Journal of Pharmaceutics and Biopharmaceutics - Volume 76, Issue 3, November 2010, Pages 421–427