Corrosion characteristics of reduced activation ferritic steel, JLF-1 (8.92Cr–2W) in molten salts Flibe and Flinak

Static corrosion tests were performed in molten salts, LiF–BeF2 (Flibe) and LiF–NaF–KF (Flinak), at 500 °C and 600 °C for 1000 h. The purpose is to investigate the corrosion characteristics of reduced activation ferritic steels, JLF-1 (8.92Cr–2W) in the fluids. The concentration of hydrogen fluoride (HF) in the fluids was measured by slurry pH titration method before and after the exposure. The HF concentration determined the fluoridation potential. The corrosion was mainly caused by dissolution of Fe and Cr into the fluids due to fluoridation and/or electrochemical corrosion. Carbon on the surface might be dissolved into the fluids due to the corrosion, and this resulted to the decrease of carbide on the surface. The corrosion depth of the JLF-1 specimen, which was obtained from the weight losses, was 0.637 μm in Flibe at 600 °C and 6.73 μm in Flinak at 600 °C.