H2O2/HCl and heat-treated Ti-6Al-4V stimulates pre-osteoblast proliferation and differentiation
موضوعات مرتبط
علوم پزشکی و سلامت پزشکی و دندانپزشکی دندانپزشکی، جراحی دهان و پزشکی
پیش نمایش صفحه اول مقاله
H2O2/HCl and heat-treated Ti-6Al-4V stimulates pre-osteoblast proliferation and differentiation
چکیده انگلیسی

The purpose of the present study was to evaluate the bioactivity of chemical treatment of titanium alloy (Ti-6Al-4V) in vitro. Smooth-surface discs of Ti-6Al-4V were used in this study. Sandblasted, dual acid-etched and H2O2/HCl heat-treated discs were set as test group, and sandblasted, dual acid-etched discs as control group. SEM and XRD analysis revealed a porous anatase gel layer on rough surface in the test group and a rough surface in the control group. Mouse pre-osteoblasts (MC3T3-E1 cells) were cultured on these 2 group discs, and then cell proliferation and differentiation were examined 4 days, 7 days, and 14 days after cell seeding. Cell proliferation was greatly stimulated at all time points when cultured in test group (P < .05). The alkaline phosphatase (ALP) activity and osteocalcin (OC) production were much higher in the test group compared with the control group at every time point investigated (P < .05). Furthermore, in the test group, the expressions of alkaline phosphatase-2, osteocalcin, and collagen type I alpha 1 mRNAs were significantly up-regulated as compared with those in the control group (P < .05 or P < .01). The results suggested that H2O2/HCl and heat-treatment might facilitate better integration of Ti-6Al-4V implants with bone.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Oral Surgery, Oral Medicine, Oral Pathology, Oral Radiology, and Endodontology - Volume 108, Issue 3, September 2009, Pages 368–375
نویسندگان
, , , , , ,