Utilization of hemp concrete using hemp shiv as coarse aggregate with aluminium sulfate [Al2(SO4)3] and hydrated lime [Ca(OH)2] treatment
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی عمران و سازه
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
This research presents the potential of hemp shiv for use as coarse aggregate in concrete. Hemp shiv was mineralized with aluminium sulfate Al2(SO4)3 and calcium hydroxide Ca(OH)2 before being used as a coarse aggregate to produce hemp concrete. The cement to sand ratio was 1:2, the Al2(SO4)3 to Ca(OH)2 ratio was 1:2, and the amount of superplasticizer was 1% by mass of cement. The compressive strength, density and water absorption of hemp concretes were tested. The results showed that at 28Â days the compressive strength of hemp concrete was in the range of 15.0-17.0Â MPa, density of 1420-1470Â kg/m3 and water absorption of 14.5-16.5%. The results indicated that the application of Al2(SO4)3 and Ca(OH)2 for mineralization increased the compressive strength of hemp concrete by four times compared to that with non-mineralized hemp shiv. The use of Al2(SO4)3 improved the compressive strength of composites and the increase in the amount of Al2(SO4)3 also accelerated the setting and hardening of the matrix.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Construction and Building Materials - Volume 156, 15 December 2017, Pages 435-442
Journal: Construction and Building Materials - Volume 156, 15 December 2017, Pages 435-442
نویسندگان
Saksith Pantawee, Theerawat Sinsiri, Chai Jaturapitakkul, Prinya Chindaprasirt,