Environmentally assisted fatigue behaviour of stress relieved metal inert gas (MIG) AA5083 welds in 3.5% NaCl solution
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Environmentally assisted fatigue behaviour of stress relieved metal inert gas (MIG) AA5083 welds in 3.5% NaCl solution Environmentally assisted fatigue behaviour of stress relieved metal inert gas (MIG) AA5083 welds in 3.5% NaCl solution](/preview/png/5015138.png)
چکیده انگلیسی
Environmentally assisted fatigue crack propagation behaviour of metal inert gas (MIG) welded AA5083 joints under stress relieving treatment has been investigated. In this study, 'in-process' stress relieving treatment, namely static thermal tensioning was applied during MIG welding process. Subsequently, fatigue crack propagation tests were performed in 3.5% NaCl solutions with and without a chromate inhibitor. A sinusoidal loading wave form was used in these fatigue tests with stress ratio, R and frequency, f of 0.1 and 8Â Hz respectively. For complementary tests, residual stress measurements were conducted using neutron diffraction method whereas effect of corrosive environments was assessed using potentiodynamic polarisation technique. Results showed that electrochemical corrosion characteristics of the weld metals under stress relieving treatment were improved marked by the presence of anodic passivation regions in potentiodynamic polarisation curves with reduced corrosion rates. Moreover, synergistic effect of compressive residual stress and repassivation of the weld joints seemed to inhibit environment fatigue crack propagation.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Fatigue - Volume 100, Part 1, July 2017, Pages 285-295
Journal: International Journal of Fatigue - Volume 100, Part 1, July 2017, Pages 285-295
نویسندگان
M.N. Ilman, N.A. Triwibowo, A. Wahyudianto, M.R. Muslih,