The microstructure of rubber-modified polystyrene after thermal ageing at 90 °C and multiple extrusion was analyzed by time-domain nuclear magnetic resonance (TD-NMR) in a non-destructive manner. The transverse magnetization decay behaviour observed in TD-NMR was related to the total rubber fraction and its cross-linking density. The data reveal different mechanisms of long-term rubber degradation in high-impact polystyrene (HIPS) during thermo-oxidation and multiple processing: Multiple processing causes a slight increase in the cross-linking density of the rubber phase, without appreciably altering the total amount of rubber fraction. Thermo-oxidation is accompanied by a significant overall decrease of the rubber fraction, an increase of the cross-linking density, and a pronounced increase of the non-crosslinked fraction (chain ends and fragmented segments). The NMR results correlate well with spectroscopic observations and moderately with macroscopic mechanical properties.
Journal: Polymer - Volume 52, Issue 6, 10 March 2011, Pages 1410-1416