Sulfonated polyimides bearing benzimidazole groups for proton exchange membranes

A series of sulfonated polyimides containing benzimidazole groups were synthesized using 4,4′-binaphthyl-1,1′,8,8′-tetracarboxylic dianhydride (BTDA), 4,4′-diaminodiphenyl ether-2,2′-disulfonic acid (ODADS) as the sulfonated diamine, and 2-(3′,5′-diaminophenyl)benzimidazole (a) or 6,4′-diamino-2-phenylbenzimidazole (b) as the nonsulfonated diamine. The electrolyte properties of the synthesized polyimides (Ia − x, Ib − x, x refers to molar percentage of the sulfonated diamine) were investigated and compared with those of polyimides (Ic − x) from BTDA, ODADS, and m-phenylenediamine (c). All synthesized polyimides possessed high molecular weights revealed by their high viscosity, and formation of tough and flexible membranes. Polyimides with benzimidazole groups exhibited much better swelling capacity than those without benzimidazole groups. This was attributed to the strong interchain interaction through basic benzimidazole functions and sulfonic acid groups. The sulfonated polyimides that are incorporated with 1,1′,8,8′-binaphthalimide exhibited better hydrolytic stability than that with 1,4,5,8-naphthalimide. Polyimide membranes with good water stability as well as high proton conductivity were developed. Polyimide membrane (Ia − 90), for example, did not lose mechanical properties after being soaked in boiling water for 1000 h, while its proton conductivity was still at a high level (compared to that of Nafion 117).