Morphology and mechanical properties of nanostructured blends of epoxy resin with poly(ɛ-caprolactone)-block-poly(butadiene-co-acrylonitrile)-block-poly(ɛ-caprolactone) triblock copolymer
موضوعات مرتبط
مهندسی و علوم پایه شیمی شیمی آلی
پیش نمایش صفحه اول مقاله
Morphology and mechanical properties of nanostructured blends of epoxy resin with poly(ɛ-caprolactone)-block-poly(butadiene-co-acrylonitrile)-block-poly(ɛ-caprolactone) triblock copolymer
چکیده انگلیسی

Poly(ɛ-caprolactone)-block-poly(butadiene-co-acrylonitrile)-block-poly(ɛ-caprolactone) triblock copolymer was synthesized via the ring-opening polymerization of ɛ-caprolactone with dihydroxyl-terminated butadiene-co-acrylonitrile random copolymer. The amphiphilic block copolymer was used to toughen epoxy thermosets via the formation of nanostructures. The morphology of the thermosets was investigated by means of atomic force microscopy, transmission electronic microscopy and small-angle X-ray scattering. It was judged that the formation of the nanostructures in the thermosets follows the mechanism of reaction-induced microphase separation. The thermal and mechanical properties of the nanostructured thermosets were compared to those of the ternary blends composed of epoxy, poly(butadiene-co-acrylonitrile) and poly(ɛ-caprolactone) with the identical content of the modifiers. It is noted that at the same composition the nanostructured thermosets displayed higher glass transition temperatures (Tgs) than the ternary blends, which was evidenced by dynamic mechanical analysis. The fracture toughness of the thermosets was evaluated in terms of the measurement of critical stress field intensity factor (K1C). It is noted that at the identical composition the nanostructured blends significantly displayed higher fracture toughness than the ternary blends. In addition, the K1C of the nanostructured thermosets attained the maximum with the content of the modifier less than their counterpart of ternary blending.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer - Volume 50, Issue 16, 31 July 2009, Pages 4089-4100
نویسندگان
, , , ,