Highly ordered microstructures of poly(styrene-b-isoprene) block copolymers induced by solution meniscus
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Highly ordered microstructures of poly(styrene-b-isoprene) block copolymers induced by solution meniscus Highly ordered microstructures of poly(styrene-b-isoprene) block copolymers induced by solution meniscus](/preview/png/5187738.png)
چکیده انگلیسی
Microstructures of hundreds of micron thick poly(styrene-block-isoprene) copolymer films solution-cast in a cylindrical tube with the solvent evaporation controlled were investigated by transmission electron microscope (TEM), small angle X-ray scattering (SAXS) and optical microscope (OM). In a block copolymer with cylindrical polyisoprene microdomains, the orientation of the cylinders was varied along radial direction of the cylindrical tube. Highly aligned hexagonal arrays of in-plane polyisoprene cylinders were formed with their cylindrical axis parallel to the circumference of the tube in the regimes close to the wall edge. In contrast randomly ordered microdomains were observed at the center of the tube. We have also found that the orientation depends on the solvent evaporation rate and an intermediate rate (â¼2.3Â nL/s) provides the best orientation. In the case of a block copolymer with a bicontinuous double gyroid structure, we obtained a globally ordered microstructure where [111] crystallographic direction was parallel to the circumference of the tube. For both block copolymers, the area of highly ordered arrays of nanoscopic domains is over 1Â mm2. Development of the orientation was explained by coupling two orthogonal fields: (1) The flow of a solution induced by strong capillary force at a meniscus between the cylindrical tube wall and the block copolymer solution and (2) the solvent evaporation.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer - Volume 46, Issue 21, 7 October 2005, Pages 9133-9143
Journal: Polymer - Volume 46, Issue 21, 7 October 2005, Pages 9133-9143
نویسندگان
Jiyoung Hwang, June Huh, Bumsuk Jung, Jae-Min Hong, Min Park, Cheolmin Park,