Synthesis and properties of novel poly(tetramethylsilnaphthylenesiloxane) derivatives
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Synthesis and properties of novel poly(tetramethylsilnaphthylenesiloxane) derivatives Synthesis and properties of novel poly(tetramethylsilnaphthylenesiloxane) derivatives](/preview/png/5189840.png)
چکیده انگلیسی
Novel poly(tetramethylsilnaphthylenesiloxane) derivatives were synthesized and characterized by differential scanning calorimetry (DSC), thermogravimetry (TG), and X-ray diffraction analyses. Poly(tetramethylsilnaphthylenesiloxane) derivatives were obtained by condensation polymerization of the corresponding disilanol derivatives, i.e. 1,4-, 1,5-, 2,6-, and 2,7-bis(dimethylhydroxysilyl)naphthalenes, which were prepared by the Grignard reaction using chlorodimethylsilane and the corresponding dibromonaphthalene derivatives followed by the hydrolyses, catalyzed by palladium on charcoal. The obtained poly(tetramethyl-1,5-silnaphthylenesiloxane) was insoluble in common organic solvents; however, the other polymers exhibited the good solubility in common organic solvents, such as tetrahydrofuran (THF), chloroform, dichloromethane, and toluene. The introduction of tetramethyl-1,5-silnaphthylenesiloxane units into the resulting polymer was confirmed by 1H NMR spectrum of the copolymer obtained by condensation copolymerization of 1,5-bis(dimethylhydroxysilyl)naphthalene with 1,4-bis(dimethylhydroxysilyl)naphthalene. It was revealed from the DSC and X-ray diffraction measurements that poly(tetramethyl-1,5-silnaphthylenesiloxane) and poly(tetramethyl-2,6-silnaphthylenesiloxane) exhibited the crystallinity; however, poly(tetramethyl-1,4-silnaphthylenesiloxane) and poly(tetramethyl-2,7-silnaphthylenesiloxane) were amorphous. The glass transition temperature (Tg) and the temperature at 5% weight loss (Td5) of poly(tetramethylsilnaphthylenesiloxane) derivatives with dimethylsilyl group at 1-position of the naphthylene moiety were higher than those at 2-position of the naphthylene moiety. The Tg and melting point (Tm) of the present polymers were higher than those of poly(tetramethyl-1,4-silphenylenesiloxane).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer - Volume 46, Issue 23, 14 November 2005, Pages 9714-9724
Journal: Polymer - Volume 46, Issue 23, 14 November 2005, Pages 9714-9724
نویسندگان
Yumiko Otomo, Yu Nagase, Nobukatsu Nemoto,