عنوان انگلیسی مقاله ISI
Effects of processing history and annealing on polymorphic structure of nylon-6/montmorillonite nanocomposites
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effects of processing history and annealing on polymorphic structure of nylon-6/montmorillonite nanocomposites Effects of processing history and annealing on polymorphic structure of nylon-6/montmorillonite nanocomposites](/preview/png/5191127.png)
چکیده انگلیسی
The effects of processing history and annealing treatment on the thermal property and polymorphic structure of nylon-6/clay nanocomposites (NCNs) have been investigated. The nanocomposites, including intercalated and exfoliated ones, were prepared by extruding nylon-6 (N6) with sodium montmorillonite (Na-MMT) or organo-montmorillonite (OMMT), respectively. DSC analysis revealed multiple melting endotherms in either the extruded or the injection-molded N6 and NCNs samples. It has been observed that a small exothermic peak around 195 °C just before the lower melting peak in the skin regions. We demonstrated that this sub-Tm transition was directly related to the processing-induced shear stresses. WAXD analysis was further performed to characterize the polymorphic structure of injection-molded N6 and NCNs before and after annealing. Annealing at a temperature (80 °C) above the Tg of N6 resulted in increase of the absolute content of γ-form in the skin regions and of the relative content of γ-form in the core regions of NCNs. In particular, annealing only leaded to increase the fraction of γ-form in the exfoliated N6/OMMT nanocomposites, which might be related to a confining effect of MMT platelet on the polymer chains mobility.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer - Volume 46, Issue 14, 27 June 2005, Pages 5417-5427
Journal: Polymer - Volume 46, Issue 14, 27 June 2005, Pages 5417-5427
نویسندگان
Shaobo Xie, Shimin Zhang, Huiju Liu, Guangming Chen, Meng Feng, Huaili Qin, Fosong Wang, Mingshu Yang,