Phase behavior and hydrogen bonding in biomembrane mimicing polyurethanes with long side chain fluorinated alkyl phosphatidylcholine polar head groups attached to hard block

To achieve a good biocompatibility, two sets of novel segmented polyurethanes, namely, poly(ether urethane)s and poly(carbonate urethane)s, with long side chain fluorinated alkyl phosphatidylcholine polar head groups attached to hard block have been synthesized recently in our laboratory by using a new diol with a long side chain fluorinated alkyl phosphatidylcholine polar head group 2-[2-[2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9-hexadecafluoro-10-ethoxy-decyloxy]-N-(2-hydroxy-1-hydroxymethyl-1-methyl-ethyl)-acetamide] phosphatidylcholine, HFDAPC as an extender. These novel polyurethanes have shown a potential to be used as bio-membrane mimicry. In this article we investigated the phase behavior of these materials by Instron, DSC, DMA, and AFM because the phase behavior has a great effect on the surface properties thus the biological-related perspective. Tg decreases first then increases for the poly(carbonate urethane)s, but increases first then decreases for the poly(ether urethane)s with an increasing in fluorinate phosphatidylcholine content. On the other hand, the tensile modulus was found decrease for the poly(carbonate urethane)s but increase for the poly(ether urethane)s with an increasing in fluorinate phosphatidylcholine content. It was found via AFM that the phase separation increases in poly(ether urethane)s but phase mixing increases in poly(carbonate urethane)s, with increasing content of fluorinated phosphatidylcholine side chain. The interaction between hard and soft segment, particularly, the hydrogen bonding was investigated by FTIR. The effect of fluorinated phosphatidylcholine side group on the phase separation of polyurethane was discussed and compared with that of fluorinated polyurethanes containing only fluorinated side chains. Our result demonstrated how the phase behavior of polyurethanes could be controlled by tailoring the interaction between hard and soft segment.