The effects of reprocessing cycles on the structure and properties of isotactic polypropylene/cloisite 15A nanocomposites

The effects of reprocessing cycles on the structure and properties of isotactic polypropylene (PP)/Cloisite 15A (OMMT) (5 wt. %) nanocomposites was studied in presence of maleic anhydride-grafted-polypropylene (PP-g-MA) (20 wt. %) used as the compatibiliser to improve the clay dispersion in the polymer matrix. The various nanocomposite samples were prepared by direct melt intercalation in an internal mixer, and further they were subjected to 4 reprocessing cycles. For comparative purposes, the neat PP was also processed under the same conditions. The nanocomposite structure and the clay dispersion have been characterized by wide angle X-ray scattering (WAXS), transmission electron microscopy (TEM) and rheological measurements. Other characterization techniques such as Fourier transform infrared spectroscopy (FT-IR), tensile measurements, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) have also been used to evaluate the property changes induced by reprocessing. The study showed through XRD patterns that the repetitive reprocessing cycles modified the initial morphology of PP/OMMT nanocomposites by improving the formation of intercalated structure, especially after the fourth cycle. Further, the addition of PP-g-MA promoted the development of intercalated/exfoliated silicate layers in the PP matrix after the second cycle. These results are in agreement with TEM observations indicating an improved silicate dispersion in the polymer matrix with reprocessing cycles displaying a morphology with both intercalated/exfoliated structures. The initial storage modulus (G′) of the nanocomposites, which was highly improved in presence of PP-g-MA seems to be less affected by reprocessing cycles at very low frequencies exhibiting a quasi-plateau compared to pristine PP/OMMT and PP. In contrast, the complex viscosity was found to decrease for the whole samples indicating that the main effect of reprocessing was a decrease in the molecular weight. Moreover, the thermal and mechanical properties of the nanocomposites were significantly reduced after the first cycle; nevertheless they remained almost unchanged during recycling. No change in the chemical structure was observed in the FT-IR spectra for both the nanocomposites and neat PP samples after 4 cycles.