Flame retardation of glass-fibre-reinforced polyamide 6 by a novel metal salt of alkylphosphinic acid

Aluminum salts of phosphinic acid mixture of diisobutylphosphinic acid and monoisobutylphosphinic acid (HPA-2TBA-Al) and glass fibres were compounded with polyamide 6 to prepare a series of flame retardant GF/PA6 composites via melt blending. The flame retardance and burning behaviors of the composites were investigated by limiting oxygen index (LOI), vertical burning test (UL-94), and Cone calorimeter test. The thermal properties and decomposition kinetics were investigated by thermogravimetric analysis (TGA) under N2 atmosphere. Addition of HPA-2TBA-Al results in an increased LOI value, a UL-94 V-0 rating together with a decrease in both the values of PHRR and THR in Cone calorimetric analysis. Visual observations and scanning electronic microscopy (SEM) after flame retardant tests confirmed the char-formation which acts as a fire barrier in condense phase. Analysis of cone calorimeter data indicates that gas phase flame retardant mechanism exists in the GFPA6/HPA-2TBA-Al system.