Preparation and thermal degradation kinetics of terpolymer poly(ɛ-caprolactone-co-1,2-butylene carbonate)

Poly(ɛ-caprolactone-co-1,2-butylene carbonate) (PBCCL) was successfully synthesized via terpolymerization of carbon dioxide, 1,2-butylene oxide(BO) and ɛ-caprolactone (CL). A polymer-supported bimetallic complex (PBM) was used as catalyst. The influences of various reaction conditions such as reaction content, reaction time and reaction temperature on properties of terpolymers were investigated. When CL content increased, the viscosity-average molecular weights (Mv), glass transition temperature (Tg) and decomposition temperature (Td) of PBCCL improved relative to those of poly(1,2-butylene carbonate) (PBC). Prolonging the reaction time resulted in increase in Mv and Tg. As reaction temperature increased, the molar fractions of CL (fCL) increased obviously. When the reaction temperature went beyond 80 °C, the resulting copolymers tended to be crystalline. The thermal properties and degradation behaviors of PBCCL were investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The apparent activation energy and thermal degradation model of PBCCL was estimated by means of Ozawa-Flynn-Wall method and Phadnis-Deshpande method, respectively. The results showed that Tg and Td of the terpolymer PBCCL were much higher than those of PBC. The thermal degradation behavior of PBCCL was evidenced by one-step thermal degradation profile. The average apparent activation energy is 77.06 kJ/mol, the thermal degradation kinetics follows the power law thermal decomposition model.