Biobased myo-inositol as nucleator and stabilizer for poly(lactic acid)

myo-Inositol made from a biomass feedstock was used as an additive for poly (l-lactic acid) (PLLA) which was also made from biomass feedstock. The crystallization and stabilization of PLLA by the addition of myo-inositol were evaluated by the melt injection molding process. While the isothermal crystallization of PLLA at 100 °C had finished over 14 min after melting, that of PLLA with 5 wt% myo-inositol finished within 2 min. The crystal growth of PLLA started when the myo-Inositol crystal was added, and the crystallization was promoted. Furthermore, the molecular weight of PLLA with myo-inositol did not decrease during the melt-mixed at 200 °C, different from that of PLLA without the myo-inositol. myo-Inositol prevented the degradation of PLLA during the thermal melting process. The biomass carbon ratio measured by the accelerator mass spectroscopy method showed that the PLLA with 5 wt% myo-inositol was a fully biobased material. It was demonstrated that myo-inositol was a multi-functional biobased additive for the modification of PLLA without decreasing its mechanical properties.