An assessment of the role of morphology in thermal/thermo-oxidative degradation mechanism of PP/EVA/clay nanocomposites

In this study, morphological properties of polypropylene (PP)/ethylene vinyl acetate copolymer (EVA) (75/25 wt/wt) blend-based nanocomposites containing various amounts of organically modified montmorillonite (OMMT) were primarily investigated. The incorporation of compatibilizer into nanocomposites decreased EVA droplet size in PP matrix while increasing compatibilizer/OMMT ratio showed a dual behavior with respect to the variations of OMMT interlayer spacing. By a rough estimation it was found that at EVA droplet size of Dn = 0.43 μm, the highest OMMT interlayer spacing would be acheived. Increasing Dn had a negative effect on the OMMT interlayer spacing. Activation energy of thermal/thermo-oxidative degradation based on Flynn model was obtained. Isothermal degradation test was also performed and desired temperature range for predicting degradation behavior was obtained by means of a free prediction model. An attempt was made to establish a correlation between morphological and thermal/thermo-oxidative parameters and also charred residue morphology. A mechanism for degradation process was proposed according to the changes of chemical bonds during the degradation process probed by FTIR analysis.