We successfully modified organic clays containing the urethane group by introducing a covalent bond between the silanol group on the clay side and the hydroxyl group of organic modifier in the silicate layer using 1,6-diisocyanatohexane (HDI), namely surface-treated montmorillonite (30BM), to increase both basal spacing and the favorable interaction between clay and polymer. The effect of the surface urethane modification of clay on poly (butylene succinate) (PBS)/30BM nanocomposites was studied. The results of transmission electron microscopy micrographs at a 10-nm resolution and X-ray diffraction measurements allowed us to examine the degree of the high exfoliation and the effect of surface urethane modification on clay dispersibility. As results of high exfoliation, PBS/30BM nanocomposites not only exhibited the high thermal properties, but also showed a remarkable increase in physical properties (e.g., tensile strength, Young's modulus, elongation at break) due to enhanced affinity between the clay and PBS matrix. Over all, the results suggest that wide gallery spacing and the predominant affinity between PBS and clay must be considered simultaneously to increase the degree of exfoliation and physical properties as key factors.
Journal: Polymer Degradation and Stability - Volume 94, Issue 12, December 2009, Pages 2163-2169