Properties of poly(vinyl chloride)/wood flour/montmorillonite composites: Effects of coupling agents and layered silicate

Organomodified montmorillonite (OMMT) was prepared using cetylalkyl trimethyl amine bromide. OMMT and wood flour (WF) were surface-modified by silane coupling agent. They were melt-blended with polyvinyl chloride (PVC) and extruded into wood-plastic composite samples using one conical twin screw extruder. The effects of their contents on the composite mechanical properties were investigated. X-ray diffraction, transmission electron microscopy and scanning electron microscopy observed intercalation and dispersion of the OMMT. FTIR and X-ray photoelectron spectroscopy were used to analyze the silane-modification effects. The possible reaction mechanisms were proposed. After wood flour was modified by 1.5 phr silane, the impact strength and the tensile strength of wood flour-PVC composite were increased by 14.8% and 18.5%, respectively. Mechanical tests showed that the addition of OMMT did not enhance the untreated wood flour-PVC composites. However, adding 0.5% OMMT did improve the mechanical properties of the treated ones. The grafting improved the interfacial compatibility between components producing higher properties of the composites. Further addition of OMMT reinforced the composites. Too higher contents of silane and OMMT impaired some properties because of weak interfacial layer and higher concentrated stress. Cone calorimetry showed that the fire flame retardancy and smoke suppression of composites were strongly improved with the addition of OMMT.