Morphology, thermal stability and visco-elastic properties of polystyrene-poly(vinyl chloride) blends

The morphology, thermal and mechanical properties of polystyrene (PS) blends with 2.5-20 wt% of poly(vinyl chloride) (PVC) have been studied. The measurement of the glass transition temperature (Tg) from the maxima of tan δ data using dynamic mechanical thermal analysis showed that the blends were incompatible and homogenously distributed only within a limited range of PVC contents in PS. The value of the storage modulus was found to increase initially but then decreased with further addition of PVC in the matrix. Distribution of the phases in the virgin and degraded blends was also studied through scanning electron microscopy. The thermogravimetric studies on these blends were carried out under inert atmosphere from ambient to 800 °C at different heating rates varying from 2.5 to 20 °C/min. The thermal decomposition temperatures of blends were found higher than that of pure PS which indicated the stabilizing effects of PVC on PS. The effect varies with the heating rates and the composition of the blends and the phenomenon has been explained due to changing morphology of the blends with composition and the degradation time which affect the interfacial interaction between the degrading products from the polymer components. The kinetic parameters of the degradation process calculated from a method described by Ozawa have been reported for these blends.