Material propertiesLow temperature fracture toughness of PMMA and crack-tip conditions under flat-tipped cylindrical indenter
موضوعات مرتبط
مهندسی و علوم پایه شیمی شیمی آلی
پیش نمایش صفحه اول مقاله
Material propertiesLow temperature fracture toughness of PMMA and crack-tip conditions under flat-tipped cylindrical indenter
چکیده انگلیسی

Fracture toughness of a PMMA (poly(methyl methacrylate)) plate was measured at −20°C, −40°C and −80°C, using a newly-developed flat-tip indentation method, and compared with the room temperature results. A flat-tipped cylindrical indenter with a sharp edge, made from hardened steel, was used for the experiments. For comparison, indentation damage and crack patterns from a tungsten-carbide tip with a microscopically-chipped edge were also examined. The zigzag imprint front shows indentation cracking can indeed be generated under a flat-tipped indenter, as implied by the theoretical singular stress field at the contact edge of a sharp-edged and flat-tip indenter. Finite element analysis (FEA) simulations were used to confirm the theoretical fracture toughness equations for pure elastic stress fields, and were used to determine the elastic stress field at the indentation crack-tip following the theoretically-determined cracking angle to illustrate the nature of the mixed-mode elastic fracture. However, as shown by optical cross-section observations, plastic damage in PMMA at the contact edge alters the cracking/damage pattern.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer Testing - Volume 38, September 2014, Pages 57-63