![عکس صفحه اول مقاله: Poly(N,N-dimethylaminoethyl methacrylate)/graphene oxide hybrid hydrogels: pH and temperature sensitivities and Cr(VI) adsorption Poly(N,N-dimethylaminoethyl methacrylate)/graphene oxide hybrid hydrogels: pH and temperature sensitivities and Cr(VI) adsorption](/preview/png/5209905.png)
Different amounts of graphene oxide (GO) were incorporated to N,N-dimethylaminoethyl methacrylate (DMAEMA), fabricating a series of pH and temperature dual sensitive PDMAEMA/GO hybrid hydrogels by in situ polymerization. Their microscopic network structures as well as swelling properties and Cr(VI) adsorption were characterized. The equilibrium swelling ratios (ESR) of hydrogels increased significantly with 0.5 wt% GO feeding of DMAEMA amount, and then decreased with further GO loading increasing. All hydrogels showed obvious deswelling when pH value of swelling mediums increased from 5 to 10 gradually. At pH 7, hydrogels revealed slight ESR increment with temperature up to 50 °C, above which obvious deswelling occurred. In pH 8 buffer, 0.5 wt% of GO loading triggered lower critical solution temperature (LCST) to decrease by 3 °C, and 2-7 °C increment was observed when 1-6 wt% of GO was loaded, as compared with that of GO-free PDMAEMA hydrogel. Cr(VI) adsorption of hydrogels was also improved by the introduction of GO to some extent, and the maximum Cr(VI) adsorption of 180 mg/g was realized, indicating that the obtained PDMAEMA/GO hybrid hydrogels possess excellent adsorption performance.
Journal: Reactive and Functional Polymers - Volume 81, August 2014, Pages 8-13