Surface analysis and mechanical behaviour mapping of vertically aligned CNT forest array through nanoindentation

Carbon nanotube (CNT) based architectures have increased the scientific interest owning to their exceptional performance rendering them promising candidates for advanced industrial applications in the nanotechnology field. Despite individual CNTs being considered as one of the most known strong materials, much less is known about other CNT forms, such as CNT arrays, in terms of their mechanical performance (integrity). In this work, thermal chemical vapor deposition (CVD) method is employed to produce vertically aligned multiwall (VA-MW) CNT carpets. Their structural properties were studied by means of scanning electron microscopy (SEM), X-Ray diffraction (XRD) and Raman spectroscopy, while their hydrophobic behavior was investigated via contact angle measurements. The resistance to indentation deformation of VA-MWCNT carpets was investigated through nanoindentation technique. The synthesized VA-MWCNTs carpets consisted of well-aligned MWCNTs. Static contact angle measurements were performed with water and glycerol, revealing a rather super-hydrophobic behavior. The structural analysis, hydrophobic behavior and indentation response of VA-MWCNTs carpets synthesized via CVD method are clearly demonstrated. Additionally, cycle indentation load-depth curve was applied and hysteresis loops were observed in the indenter loading-unloading cycle due to the local stress distribution. Hardness (as resistance to applied load) and modulus mapping, at 200 nm of displacement for a grid of 70 μm2 is presented. Through trajection, the resistance is clearly divided in 2 regions, namely the MWCNT probing and the in-between area MWCNT − MWCNT interface.