Comparative analysis of thermally induced degradation of condensation-grown (1Â 0Â 0)Ge0.75Si0.25/SiO2 interfaces by electron spin resonance
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Comparative analysis of thermally induced degradation of condensation-grown (1Â 0Â 0)Ge0.75Si0.25/SiO2 interfaces by electron spin resonance Comparative analysis of thermally induced degradation of condensation-grown (1Â 0Â 0)Ge0.75Si0.25/SiO2 interfaces by electron spin resonance](/preview/png/5353569.png)
چکیده انگلیسی
An electron spin resonance study has been carried out on the influence of isochronal annealing on the GeSi/SiO2 interfaces of the condensation grown (1 0 0)Si/SiO2/Ge0.75Si0.25/SiO2 structure. The thermal interface stability has been monitored in terms of the evolution of occurring paramagnetic interface defects, in particular, here involving the Ge dangling bond GePb1 point defect, previously identified as a detrimental interface trap. This reveals thermal post-growth interface degradation, initiating from annealing at the temperature â¼440 °C onward, identified as substantial generation of GePb1 interface traps in addition to those naturally introduced into the system during sample manufacturing. In terms of GePb1 density, the interface thus appears only robust for thermal treatment in vacuum up to 440 °C. For Tan reaching â¼520 °C, a drastic degradation occurs as exposed by an about two-fold increase in GePb1 density, which state is maintained up to Tan â¼Â 900 °C. Annealing in H2 (â¼1 atm) has a similar effect, except that the interface degrades more gradually. Above 900 °C, the structure's integrity gradually collapses because of disintegration (Ge escape) of the SiGe layer. As to device implementation, the data indicate that temperatures of processing steps in O-deficient ambient should be kept below â¼440 °C.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 291, 1 February 2014, Pages 20-24
Journal: Applied Surface Science - Volume 291, 1 February 2014, Pages 20-24
نویسندگان
J. Kepa, A. Stesmans, V.V. Afanas'ev,