عنوان انگلیسی مقاله ISI
Effects of peak current density on the mechanical properties of nanocrystalline Ni-Co alloys produced by pulse electrodeposition
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effects of peak current density on the mechanical properties of nanocrystalline Ni-Co alloys produced by pulse electrodeposition Effects of peak current density on the mechanical properties of nanocrystalline Ni-Co alloys produced by pulse electrodeposition](/preview/png/5361550.png)
چکیده انگلیسی
Cobalt content, grain size, microhardness and tensile strength of nanocrystalline Ni-Co deposits produced from a solution containing saccharin and cobalt sulfate at constant electrodeposition conditions (pulse on-time Ton at 1 ms and pulse off-time Toff at 15 ms) but varying the peak current density Jp were investigated. It is found that an increase in Jp makes the deposit Co content lower, colony-like morphology more obvious, grain size smaller, and hardness and tensile strength higher. All of the facts are believed to result from the higher overpotential and nucleation rates caused by the Jp increase. But its further increase could lead to reduction in the hardness and tensile strength. Peak current densities in the range of 100-120 A dmâ2 are recommended for the preparation of nanostructured Ni-Co alloy deposits with grain sizes in the range of 15-20 nm, containing 7-8% Co, possessing hardness of 590-600 kg mmâ2 and tensile strength of 1180-1200 MPa-significantly higher than the strength of pure nickel deposit which is produced by the similar method and gets similar grain size.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 254, Issue 21, 30 August 2008, Pages 6865-6869
Journal: Applied Surface Science - Volume 254, Issue 21, 30 August 2008, Pages 6865-6869
نویسندگان
Yundong Li, Hui Jiang, Weihua Huang, Hui Tian,