A comparative in vivo evaluation of bioactive glasses and bioactive glass-based composites for bone tissue repair

- New sintered bodies (a bioglass and two composites) were tested in vivo in rabbits.
- 45S5 Bioglass® sintered powders were implanted and used as a term of comparison.
- Compared to 45S5, the new glass preserved its amorphous phase after sintering.
- The new bioglass is slightly higher osteoconductive than 45S5 glass-ceramics.
- The performance of the new bioglass is better also in terms of implant's stability.

In this work a set of novel materials for bone tissue regeneration have been tested in vivo in an animal model. In fact, despite many studies have been devoted to amorphous 45S5 Bioglass®, there is lack in the literature of works aimed to study the in vivo performance of heat-treated - and thus partially crystallized - 45S5. As widely reported, crystallization limits the bioactivity of 45S5 and is the main reason that prevents a broader use of this material. Thus, in the present work, a recently developed bioactive glass (BG_Ca/Mix) is tested, since previous investigations demonstrated that BG_Ca/Mix is particularly promising by virtue of both its high bioactivity and lower tendency to crystallize with respect to 45S5. BG_Ca/Mix sintered powders and two composites, which contain BG_Ca/Mix and an increasing percentage (20 wt% or 70 wt%) of hydroxyapatite (HA), were considered. As a term of comparison, 45S5 sintered powders were also studied. The samples were implanted in rabbits' femurs and harvested after 8 weeks. The histological analysis demonstrated that BG_Ca/Mix has an osteoconductive ability slightly higher than that of 45S5 glass-ceramics, followed by that of the composites, which may represent the starting point for obtaining systems with degradation rate tailored for a given clinical application. Moreover, the 45S5 samples were locally cracked, probably because of a non-uniform dissolution in the physiological environment. On the contrary such cracks, which could lead to implant instability and unsuitable mechanical performance, were not observed in BG_Ca/Mix.