Dense graphene nanoplatelet/yttria tetragonal zirconia composites: Processing, hardness and electrical conductivity
ترجمه فارسی عنوان
کامپوزیت زیرکونیا تتراگونال چگالی گرافیتی نانوپلاستیک / یتریا: پردازش، سختی و هدایت الکتریکی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
چکیده انگلیسی
Yttria tetragonal zirconia ceramic composites with 1, 2.5, 5 and 10 vol% nominal contents of graphene nanoplatelets (GNPs) were fabricated and characterized. First, the GNP dispersion in isopropanol was optimized to de-agglomerate the GNPs without damaging their structure. Then, submicrometric fully dense composites were obtained via spark plasma sintering (SPS) at 1250 °C with a 5 min holding time. The processing routine produced a nearly homogeneous GNP dispersion in the ceramic matrix, and the GNPs preferential orientation was perpendicular to the sintering compression axis. A ceramic grain refinement due to the GNPs was also detected. The Vickers hardness measured on the plane perpendicular to the sintering compression axis (basal plane) was lower than on the cross sections. This anisotropy increased with the increasing GNP content, while the average hardness decreased. The electrical conductivity was also highly anisotropic, up to seven times higher for the basal planes. The electrical percolation threshold for these composites was estimated to be between 2.2 and 4.4 vol% of the GNP measured content.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 15, 15 October 2017, Pages 11743-11752
Journal: Ceramics International - Volume 43, Issue 15, 15 October 2017, Pages 11743-11752
نویسندگان
Angela Gallardo-López, Iván Márquez-Abril, Ana Morales-RodrÃguez, Antonio Muñoz, RosalÃa Poyato,