Antiferromagnetism and heat capacity of NaCo2âxCuxO4 ceramics
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Polycrystalline samples of NaCo2âxCuxO4 (x=0, 0.01, 0.03 and 0.05) were synthesized in two different ways: 1) by a mechanochemically assisted solid-state reaction method (MASSR) and 2) by a citric acid complex method (CAC). In this work we examined the influence of these synthesis routes and small Cu concentrations on magnetic properties and the heat capacity of sintered samples. The magnetic susceptibility (Ï) of all samples followed the Curie-Weiss law in the temperature range between 50 K and 300 K, while a negative Weiss constant (θ) implied an antiferromagnetic interaction. According to the magnetic susceptibility data, a peak around 30 K indicating the presence of Co3O4 as a secondary phase appeared for all MASSR samples and CAC samples with Cu content above 1%. The effective magnetic moment (μeff) of CAC samples was lower than the theoretical, spin only value obtained for the Co4+ ion in the low spin state indicating the presence of low spin Co3+(S =0). These values were also lower compared to the values obtained for MASSR samples. The highest μeff of 1.75 μB/atom Co was obtained for the undoped MASSR sample. The heat capacity of CAC samples at 2 K decreased with Cu concentration due to lowering of the electronic specific heat coefficient (γ). The highest γ of 63.9 mJ/molK2 was obtained for the undoped CAC sample. This reduction in γ values was the result of the decrease of the density of state and/or mass enhancement factor.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 2, 1 February 2017, Pages 2022-2026
Journal: Ceramics International - Volume 43, Issue 2, 1 February 2017, Pages 2022-2026
نویسندگان
Sanja PrÅ¡iÄ, Slavica M. SaviÄ, Zorica BrankoviÄ, Zvonko JagliÄiÄ, Stanislav Vrtnik, Goran BrankoviÄ,